Fatturi li jaffettwaw il-forza tal-ankraġġ ta 'spikes tat-toroq u metodi għat-titjib tagħhom
- X'inhuma l-fatturi ewlenin li jaffettwaw il-forza ta 'l-ankraġġ bil-ponta?
The strength of anchoring materials is crucial. The compressive strength of sulfur anchoring agent must be ≥40MPa; if it is lower than 30MPa, the anchoring force will decrease by 30% - 40%. The water - cement ratio must be controlled within the range of 0.3 - 0.35. The fit gap between the nail hole diameter and the spike should be moderate. An excessively large gap (>3mm) se jnaqqas il-forza tal-ankraġġ b'20% - 25%, filwaqt li hemm vojt eċċessivament żgħir (<1mm) makes it difficult for the anchoring agent to fill. The optimal gap is 1.5 - 2mm to ensure uniform wrapping force. Insufficient spike embedding depth (<100mm) will reduce the anchoring force by 40% - 50%. The standard embedding depth should be 120 - 150mm, and the embedded part must have threads or barbs to increase mechanical biting force. Insufficient pouring of anchoring agent (voids >5%) se jikkawża konċentrazzjoni ta 'tensjoni lokali, u ċ-ċaqliq tal-forza tal-ankraġġ jilħaq 15% - 20% . It-tferrigħ tal-pressjoni għandu jintuża biex jiżgura l-kumpattezza .
- X'inhuma d-differenzi fil-forza tal-ankraġġ bil-ponta fost materjali ta 'ankraġġ differenti?
Aġent tal-Ankraġġ tas-Sulfur (Sulfur: Siment: Sand=1: 0 . 3: 1 . 5) għandu forza ta 'ankraġġ ta' {60 - 80 KN Ferroviji ordinarji . aġent tal-ankraġġ tar-reżina (reżina epoxy + aġent tat-tqaddid) għandu forza ta 'ankraġġ ta' 80 - 100 kn, b'reżistenza tajba tat-temp {. Il-bidla tal-forza tal-ankraġġ hija inqas minn jew daqs 10% fil-firxa ta '- 40 - 60 grad, iżda l-ispiża tagħha hija 50%- 60% aġent, preferut għal ferroviji b'veloċità għolja u reġjuni kesħin . aġent ta 'l-ankraġġ tat-tikħil tas-siment għandu forza ta' ankraġġ aktar baxxa (40 - 60 kn) iżda protezzjoni ambjentali tajba, adattata għal tranżitu ferrovjarju urban . 5}% {- 8% 膨胀剂 għandu jkun miżjud biex jikkumpensa għal xxekk Aġent tal-ankraġġ (raża + fibra tal-azzar) għandu forza ta 'ankraġġ ta' 100 - 120 kn. Meta l-kontenut tal-fibra tal-azzar huwa 3% - 5%, is-saħħa tal-shear tiżdied b'25% - 30%, użat fit-taqsimiet ewlenin tal-ferroviji tal-ġibda tqal.
- Kif jaffettwa l-proċess tal-kostruzzjoni tal-forza tal-ankraġġ bil-ponta?
Incomplete cleaning of nail holes (residual dust >5%) se jnaqqas il-forza tal-ankraġġ bi 15% - 20% . Guns ta 'l-arja ta' pressjoni għolja għandhom jintużaw għat-tindif, u xkupilji tal-wajer għandhom jintużaw jekk meħtieġ biex jiżguraw l-ebda gagazza f'wiċċ l-ilma fuq il-ħajt ta 'ġewwa tat-toqob tad-dwiefer . Temperatura baxxa wisq ta' l-ankraġġ (<130℃ for sulfur anchoring) will lead to poor fluidity and incomplete filling, reducing the anchoring force by 25% - 30%. The pouring temperature must be controlled at 140 - 160℃. A deviation of spike insertion depth >5mm se tagħmel id-distribuzzjoni tal-forza tal-ankraġġ irregolari, u d-differenza tal-forza tal-ankraġġ ta 'spikes fl-istess lott tista' tilħaq 10% - 15% . L-għodod ta 'pożizzjonament għandhom jintużaw waqt l-inserzjoni biex tiżgura fond uniformi, b'devjazzjoni inqas minn jew daqs 3mm .<24 hours) will make the anchoring agent strength not up to standard, and the anchoring force is only 70% - 80% of the design value. Resin anchoring agent needs to be cured for more than 48 hours, and sulfur anchoring agent needs to be naturally cooled to room temperature (≥6 hours).
- Il-fatturi ambjentali kif jaffettwaw il-forza tal-ankraġġ bil-ponta?
A humid environment will reduce the bonding force between the anchoring agent and the nail hole. When the relative humidity is >90%, the anchoring force decreases by 10% - 15%. Rainy day construction must take rainproof measures to ensure that the nail hole is dry (moisture content ≤5%). A high - temperature environment (≥35℃) will accelerate the curing of resin anchoring agent, and concentrated reaction heat release may cause internal cracking, with an anchoring force loss of 20% - 25%. Retarders must be added to the anchoring agent to extend the gel time to 30 - 40 minutes. Freeze - thaw cycles (- 20 - 20℃) will cause microcracks in the anchoring agent. After 200 cycles, the anchoring force decreases by 30% - 40%. Frost - resistant anchoring agent (adding air - entraining agent, air content 3% - 5%) must be selected in cold regions. Saline - alkaline soil will erode the anchoring agent. When the chloride ion concentration is >500mg / l, il-forza tal-ankraġġ ttaffi b'5% - 8% kull sena . anti - spikes miksija bil-korrużjoni u aġent tal-ankraġġ reżistenti għall-alkali għandhom jintużaw f'żoni kostali .
- X'inhuma l-miżuri speċifiċi biex titjieb il-forza tal-ankraġġ bil-ponta?
Ottimizza l-formula tal-aġent tal-ankraġġ: Żieda ta '5% - 8% trab tal-grafita ma' aġent ta 'ankraġġ tal-kubrit jista' jżid il-forza ta 'ankraġġ b'10% - 15% u ttejjeb il-fluwidità; Iż-żieda ta '1% - 2% aġent ta' l-akkoppjar silane ma 'aġent ta' ankraġġ ta 'reżina ssaħħaħ il-forza ta' twaħħil ta 'l-interface ma' spikes . Adotta assistenza ta 'ankraġġ mekkaniku: irrumblar ta' linji oblikwi (pitch {3 - 4 mm) fuq il-wiċċ ta 'l-ankra, iżżid il-forza ta' l-ankraġġ b'20% - 25% . tqal - il-ponot tal-ferrovija tal-ġibda għandhom jadottaw din l-istruttura . Ittejjeb il-proċess ta 'kostruzzjoni: tispara minn qabel it-toqba tad-dwiefer ({40 - 50 grad) biex ittejjeb il-fluwidità tal-aġent tal-ankra, iżżid il-mili tal-kompatte Il-forza tal-ankraġġ: 10% ta 'spikes fil-ferroviji ordinarji huma kampjunati kull sentejn . dawk b'forza ta' ankraġġ inqas minn 80% tal-valur tad-disinn jeħtieġ li terġa 'tiġi ankrata . Il-ferroviji ta' veloċità għolja jiġu skoperti darba sena biex jiżguraw li l-forza ta 'ankrar tiltaqa' ma 'l-istandard (ikbar minn jew ugwali għal 60kn).}}}}}}}